Local Cuban bentonite clay: composition, structure and textural characterization

. The physic and chemical characterization of the bentonite clay from the Chiqui Gómez deposit, central Cuba, (Cuban bentonite clay) shows that it is mainly constituted by sodium montmorillonite (>90%), with a structural formula for one-layer unit determined as (Na 3.99 Al 0.01 )(Al 1.11 Fe 3+0.49 Mg 0.18 Ti 0.07 )(Ca 0.24 Na 0.15 K 0.01 )O 10 (OH) 2 . The Cuban bentonite clay has a specific surface area of 80 m 2 g -1 , a pore volume of about 0.0776 cm 3 g -1 , 61% porosity and both N 2 adsorption-desorption isotherms exhibit a hysteresis loop of IV type. The thermogravimetric analysis (TGA) of the studied mineral presents the first endothermic peak, characteristic of montmorillonite, in 48.1 ºC and others less accentuated (80.8, 94.0, 119.8 ºC) characteristic of sodium montmorillonite, that corresponds to the loss of water, and can be extended up to 250 ºC. The FT-IR spectra show the existence of Si-OH, Al-Al-OH, Al-Fe-OH, Al-Mg-OH and Si-O-Si functional groups in all clay samples, bands between 1,120 and 461 cm -1 correspond to phyllosilicate structures and OH stretching vibrations were observed. pH at the point of zero charge (pH PZC ) obtained has a value of 8.1, which allows montmorillonite to be classified as basic.


Introduction
Bentonite clays are widely distributed in the world (Grim and Güven, 1978). They are ores with montmorillonite as the main component and besides montmorillonite; bentonite contains other minerals, such as quartz, calcite, feldspar, muscovite and biotite (Pеtrоvić et al., 2014). This mineral has properties such as charge density, surface charges, surface area, the type of exchangeable cations, silanol groups of crystalline defects or broken surfaces, hydroxyl groups on the edges, and Lewis and Bronsted acidity (Djomgoue and Njopwouo, 2013) which make it have a great adsorption capacity, this is why this mineral has multiple uses in different industrial processes.
The adsorption characteristics of bentonite depend on its chemical and mineralogical composition as well as on textural, structural and morphological characteristics (Pеtrоvić et al., 2014). The use of bentonite as an adsorbent for oil impurities has been widely used and discussed in various investigations (Larouci et al., 2015). Although bentonite can be used as an adsorbent in its natural form, some researchers have proposed experimental designs and methodologies for the acid activation of these minerals in order to optimize the purification process Palanisamy et al., 2011;Ajemba, 2012;Usman et al., 2013;Larouci et al., 2015); when applying this activation method it should be borne in mind that excessive activation can be explained in terms of a loss of porosity and acid strength . Also, acid treatment of bentonites has been shown to create mesoporosity depending on the acid concentrations and time of treatment involving major structural changes and partial decomposition of montmorillonite (Zheng et al., 2017). Nadhiro et al. (2018) studied the quality of Sardinella lemuru oil using bentonite as an adsorbent, revealing that the addition of activated bentonite can increase the quality of this oil that is canned in industry; meanwhile Suseno et al. (2014) showed in his research that the combination of different concentrations of natural bentonite followed by centrifugation is an excellent technique for purifying this oil, where the oil bleaching process tends to decrease as the concentration of the adsorbent is decreased and centrifugation speed. The aim of the present study is to characterize the bentonite clays of the Chiqui Gómez bentonite deposit in Cuba (denominated as Cuban bentonite clays in this work) due to the potential of this unexploited deposit, which could be used as adsorbent of shark liver oil impurities. To this end, their mineralogy, chemistry, textural, structural and morphological characteristics were determined.

Materials
The raw clay samples ( Fig. 1) used in the present work were collected from the deposit Bentonita Chiqui Gómez (X=633,200; Y=311,350) which is located in Remedio, 44 km northeast Villa Clara in the Central Region of Cuba. The samples were provided by Empresa Geominera del Centro, which has a processing capacity of 2 Kt/year. They contain 50-60% mixed-layered illite-smectite (I-S) with 80-85% expandable layers, minor clinoptilolite, quartz, opal-CT, carbonates (calcite and trace siderite) and trace of gypsum and kaolinite.
The Bentonita Chiqui Gómez deposit or concession, is part of the Camacho Formation lithostratigraphic unit; which is an Upper Pleistocene sedimentary deposit. This is made up of sandy-clayey silts and silty clays with a grayish brown color, with intercalations of fine gravels and carbonates concretions, as well as dispersed gypsum crystals. The bentonite bearing layer can reach a thickness of up to 3 m and is distributed in the provinces of Sancti Spíritus and Villa Clara in the center of Cuba.

548
Local Cuban bentonite clay: composition, structure and textural characterization

Sample preparation
All bentonite samples (10) were dried at 105 ℃ for 4 h in a drying air oven and then were grounded using a porcelain mill to pass through a mesh size screen of 50 μm. A composite sample was formed by the combination of 10 primary samples, taking into account that samples are truly representative of the deposit. This sample was ready for chemical analysis and physical-chemical tests including the DRX analysis.

Physicochemical characterizations of the Cuban bentonite clays
The physical characterization of the bentonite is carried out from the density determination: pycnometric with glass pycnometer, apparent and apparent by imprisonment (Kaufhold et al., 2012); porosity (Tadros, 1980;Krupskaya et al., 2019), flow rate (Elo et al., 2019); compressibility (Kahr and Madsen, 1995) and tortuousness. The chemical composition of the bentonite samples was performed by atomic absorption spectroscopy (CBG 933 AA, Melbourne, Australia). This analysis of chemical composition was corroborating by Energy Dispersive Spectrometry (EDS).

Textural properties
The textural properties of the bentonite samples were determined with a Micromeritics ASAP 2020 analyzer. 0.1001 g of raw bentonite were previously degassed at 170-200 °C for 8 h. The total pore volume was measured at a relative pressure (P/P o ) from 0 to 0.99. Adsorption isotherms were determined by N 2 adsorption over the samples at -196 ºC. The Brunauer-Emmet-Teller (BET) and Barrette-Joynere-Halenda (BJH) equations were used to calculate the specific surface area and average pore diameter of the materials from nitrogen adsorption and desorption isotherms.

Scanning Electron Microscopy (SEM) and
Energy Dispersive Spectrometry (EDS) With the objective of studying their morphology, bentonite natural powder sample were examined with a scanning electron microscope PhenomProX (SEM, operated at 15 kV). The elemental chemical analysis in the film was performed using a fully integrated EDS detector and software of the mentioned microscope.

X-ray diffraction (XRD) characterization
X-Ray diffraction peaks of bentonite clay samples were measured on a Shimadzu XD-D1 diffractometer with monochromator using a Cu-Kα radiation at a scanning rate of 2º min -1 in 2θ=10-70º. The peaks observed for the catalysts were compared to standards published by JCPDS data (Joint Committee on Powder Diffraction Standards). The crystallites size was estimated by Scherrer's equation. The 2D ordered layers structure of material was verified by low angle X-ray diffraction. The patterns were recorded on a Panalytical, X'PertCelerator (50 kV voltage), using a Cu-Kα (λ=1.54183 Ǻ) as the X-ray source. The signal was recorded for 2θ=5 to 60º with a step of 0.5º s -1 . The d-spacing (100) and the unit-cell parameter a 0 were calculated from the basic equation of the Bragg law (λ/2=sen θ and 2.d 100 /√3 respectively).

Thermal analysis
The thermal behavior of the bentonite clays was studied in a Mettler Toledo TGA/SDTA 851 instrument. The weight changes and the differential thermal process of the material (10 mg of samples) were analyzed from 25 up to 1,000 °C with a heating rate of 10 °C min -1 in air flow (80 ml min -1 ).

Fourier transform infrared (FT-IR) spectro-
photometry FT-IR Spectrophotometer Shimadzu IR Prestige 21™ (Germany) was used to analyze bentonite clay samples. Spectra ranges were set at 4,000 to 400 cm −1 , using the IRsolution Agent software. The resulting spectra were directly compared with the reference library databases.

Determination of point of zero charge and
Boehm titration The acidity and total basicity of the bentonite is determined using the Boehm method (Boehm, 1966(Boehm, , 2002Rezma et al., 2019). pH pzc is the pH at which the net particle charge becomes zero, it is an important parameter for describing surface behavior. Initial pH values (pH i ) of 20 mL of KCl solutions (concentrations 10 -3 and 10 -2 mol L -1 ) were adjusted in pH range of 3.1 to 10 using 0.01 mol L -1 of HCl or NaOH. Then, 0.05 g of Cuban bentonite clays was added to each sample. Equilibration was carried out by shaking, in a rotary incubator at 200 rpm for 2h at 25±1 ºC. The dispersions were then filtered and the final pH of the solutions (pH f ) was determined, point of zero charge was found from a plot of pH f versus pH i .

Statistical analysis
Results were expressed as mean values ± standard deviation (SD) (n=3). The R statistical software package (version 3.6.3) and Stat Graphics Centurion XV (version 15.2.06) was used to generate the orthogonal matrix of the design, response surface methodology modeling, statistical analysis, and regression models.

Characterization of the Cuban bentonite clays
The results obtained in the physical characterization are presented in table 1.The studied material presents a pycnometric density in the range reported by Quintana (2013) for cuban bentonite clay; likewise the apparent density by trapping indicates that it can be compressed practically by 50%. Bentonite clays studied presents a relatively high porosity value, above 50%, a manifestation of its high roughness and capillary action. The compressibility demonstrates the high degree of compaction, as it reduces its original volume to almost a quarter. The tortuousness values reflect a high degree of disorder of the channels and surface of the solid. The value of the flow velocity obtained (V f equal to zero) corroborates the relative high value of porosity.
The N 2 adsorption-desorption isotherms of the Cuban bentonite clay (Fig. 2) exhibit a hysteresis loop of IV type (Zhang et al., 2016). Such hysteresis loops are related to slit-shaped pores or ink-bottle pores (Fig. 2). The specific surface area of the Cuban bentonite clay (80 m 2 g -1 ) is in the lower range of the values reported by Hevia (2007) and Romero and Barrios (2006) 1 . Compared to the values reported by Hernández et al. (2003) for partially destroyed montmorillonite and quartz (325 m 2 g -1 ) and, montmorillonite and quartz (303 m 2 g -1 ) from Tehuacán, Puebla in Mexico this value is considered relatively low. However, it is slightly lower than the value reported by León Barrios and Díaz Díaz (2019) for a Na bentonite from the Manuagua deposit in La Habana province, Cuba (102 m 2 g -1 ). Aditionally, the natural bentonite from Santa Catarina State, in Brazil studied by Foletto et al. (2013) displays a specific surface area of 16.45 m 2 g -1 , substantially lower than the result obtained for the bentonite considered in this study, so the value obtained in our research would be high, a similar result is also observed in raw bentonite from Hammam Boughrara (Maghnia, Algeria) that shows a specific surface area of 29.23 m 2 g -1 (Korichi et al., 2009). Pore volume was 0.0776 cm 3 g -1 for Cuban bentonite clay.
The X-ray diffractogram of raw bentonite shows that the main mineralogical component is montmorillonite (>90%) together with minor amounts of plagioclase, cristobalite, calcite and almost undetectable presence of quartz (Fig. 3). XRD peaks are assigned according to the literature (Chihi et al., 2019;Gan et al., 2019). This analysis allows verifying the presence of dioctahedral smectite (spaced d: 14.65 Å, 4.39 Å, 4.13 Å and 2.53 Å) as the main component, and feldspar (d: 3.08 Å) correspondent to albite-anortite series (Ab-30% and An-70%) as minor phase. The diffraction signal d 060 makes it possible to distinguish between di-octahedral and tri-octahedral smectites, because the dimension of the cell on the b axis is sensitive to the size of the cations and the occupation of the sites in the octahedral layer (Moore and Reynolds, 1997;Zhou et al., 2018). The value of d 060 =1.50 Å is typical and confirms the di-octahedral character, deduced from the structural formula, and from the information obtained by chemical analysis, where the Si/Al ratio indicated a characteristic value for this type of smectites.
The thermogravimetric analyses (TGA) verify the presence of the montmorillonite in the sample under study. The analyzed sample presents the first endothermic peak, characteristic of montmorillonite, at 48.1 ºC and others less accentuated (80.8, 94.0, 119.8 ºC) characteristic of sodium montmorillonite, that correspond to the loss of water, and can be extended up to 250 ºC. The small peak at 406.7 ºC represents the loss of water from the montmorillonite hydroxyl, specifically from calcium. So at 579.7 ºC, a small endothermic reaction can be observed, which may indicate the initial stage of transformation of montmorillonite, decomposition or phase change of an impurity. The weight loss was around 9.5%, which means the percentage of water in the sample and is less than the content reported, for example, by Neira et al. (2007) for Colombian bentonite.
The FT-IR spectrum of Cuban bentonite clay (Fig. 4) reveals the bands belonging to montmorillonite: those assigned to Si-O in-plane and out-of-plane stretching vibrations at 1,050 to 1,118 cm -1 , respectively, as well as the ones corresponding to bending vibrations of Al-Al-OH, Al-Fe-OH and Al-Mg-OH at 917, 875, 840 cm -1 , respectively (Kaufhold et al., 2002;Madejová, 2003;Gereli et al., 2006;Klinkenberg et al., 2006;Madejová et al., 2006;Tyagi et al., 2006;Scholtzová et al., 2014). The spectrum obtained has the characteristic appearance of clay minerals and in particular of smectites. The bands between 1,120 and 461 cm -1 correspond to phyllosilicate structures. Three well differentiated regions are observed. In the area with the highest wave numbers (3,600 to 3,400 cm -1 ) OH stretching vibrations are identified, that can arise from the isomorphic substitution in the tetra and octahedral layers in bentonite (Wilson, 1994), occasionally in 3,424 cm -1 a slightly wide band is observed denoting the presence of water absorbed or united by elements Al and Mg (Chukanov and Chervonnyi, 2016). The area with the lowest wave values (518-461 cm -1 ) indicates the characteristic stretch vibrations of Si-O (518 cm -1 ) and deformation Si-O-Si (461 cm -1 ). The aluminum character of the octahedral layer is manifested by the intensity of the absorption band centered at 1,031 cm -1 , which is assigned to the deformation of Al-Al-OH bonds (Jafar et al., 2015).
The pH at the point of zero charge (pH PZC ) obtained has a value of 8.1, which allows montmorillonite to be classified as basic; this indicates the possibility of adsorbing metal ions and confirms the classification as sodium (Ijagbemi et al., 2009). Also important was the fast equilibration observed for successive increments of HCl during the titration process. This may suggest a relatively short time of adsorption, making negligible the effects of other processes such as dissolution that could affect proton adsorption especially at low pH (Duc et al., 2005). The fast equilibration, leading to rapid pH stability can be interpreted as a result of reactions between protons and hydroxylated surface sites which are known to be very fast reactions (Unger, 1979;Thissen, 2020). A similar behavior was observed during the acidbase potentiometric titrations with different KCl electrolyte concentrations to measure the proton adsorption (Ijagbemi et al., 2009).

Elemental analysis
The chemical composition of the analyzed samples is presented in table 2.
On the basis of the elemental analysis of the montmorillonite, obtained by the average of EDX  chemical analysis (Fig. 5), the resulting structural formula is: (Na 3.99 Al 0.01 )(Al 1.11 Fe 3+ 0.49 Mg 0.18 Ti 0.07 ) (Ca 0.24 Na 0.15 K 0.01 )O 10 (OH) 2 and indicate the location of the different cations in metal oxide octahedrons or tetrahedrons, respectively. Aluminum was assigned to tetrahedral positions to complete an occupancy of eight, then magnesium and iron were assigned to octahedral sites and completed an occupancy of four, sodium ions were assigned to the interlayer. The resulting formula represents a Wyomingtype montmorillonite (sodium montmorillonite), according to the classification by Schultz (1969), because of the layer charge, lower than 0.85 electron charges per unit cell (e − /u.c.), and the percentage of tetrahedral substitution.
The bentonite under study is a montmorillonite with low isomorphic substitution in the tetrahedral layer. The number of atoms in the octahedral layer is very close to the theoretical value of 2.0 for a dioctahedral mineral and the number of interlamina cations (0.40) is also very close to the reported 0.33. The layer load is -0.57, a value that is in the range of -0.2 to -0.6 established as a classification criterion and the load balance is practically zero (0.07). The dominant ion in the octahedron is aluminum, so it can be considered that it is an aluminum dioctahedral montmorillonite. The previous results are in line with those obtained by other authors (Jones and Handreck, 1967;Wazamtu et al., 2013), in similar works, regarding the presence of high percentage values of silica, followed by alumina and iron oxide, the latter being influential in the coloration of the sample, the oxides of magnesium and calcium are higher than those of potassium and sodium. They also have lower percentages of titanium oxide, frequently found in clays (Chihi et al., 2019;Deepracha et al., 2019). The relationship between the Si/Al ratios obtained is 4.25, which is much higher than the range reported by Daza et al. (2004) and Enciso et al. (2005) for clay of the bentonite types in Colombia. The highest oxide percentages correspond to SiO 2 and Al 2 O 3 , which together with that of Fe 2 O 3 , correspond to those reported by Chihi et al. (2019). When comparing the chemical composition of the studied sample with that of sodium and calcium bentonite types (Abdullahi and Audu, 2017), some correspondence with both can be observed in terms of SiO 2 and Al 2 O 3 contents. However, the Fe 2 O 3 content is lower than that reported for the two previously mentioned bentonite types, but closer to those of calcium rich ones. Na 2 O content is half of that reported for sodium rich bentonite, while the CaO content duplicates the reported values for the same type of bentonite, but in the range of those reported by Quintana (2013) for Cuban bentonites. Scanning electron microscopy analyzes allowed determining the morphology of the starting mineral (Fig. 5). The micrograph of the bentonite under study allowed observing dispersed particles of different sizes, no larger than 10 μm. The lamellar aggregates joined by coalescence forming a flake-shaped structure can be seen in detail. The presence of rolled tubular laminar shapes confirms the dioctahedral character of the bentonite under study. From the results obtained by the different methods and the analysis of the calculated structural formula, it is concluded that the bentonite under study is mainly composed by sodium montmorillonite, with a specific surface area of 80 m 2 g -1 and 61% of porosity.
Finally, the chemical composition and physical properties of the studied bentonite indicate that it is suitable for use in the purification of oils (Maskan and Bagci, 2003).

Conclusions
The physic and chemical characterization of the Cuban bentonite clays shows that it is mainly constituted by sodium montmorillonite (>90%), with a structural formula for one-layer unit determined as (Na 3.99 Al 0.01 )(Al 1.11 Fe 3+ 0.49 Mg 0.18 Ti 0.07 ) (Ca 0.24 Na 0.15 K 0.01 )O 10 (OH) 2 . The studied bentonite has a specific surface area of 80 m 2 g -1 , a pore volume of about 0.0776 cm 3 g -1 , 61% porosity and both N 2 adsorption-desorption isotherms exhibit a hysteresis loop of IV type. These characteristic indicate that Cuban bentonite is suitable for use in oil purification.